ASTM A53 / ASTM A106
級别: 20# 規格: 外徑X Sch No.
Size |
Size
|
Size
|
|
1/8”x Sch40
|
1”x Sch40
|
3”x Sch40
|
|
1/8”x Sch80
|
1”x Sch80
|
3”x Sch80
|
|
1/4”x Sch40
|
1-1/4”x Sch40
|
4”x Sch40
|
|
1/4”x Sch80
|
1-1/4”x Sch80
|
4”x Sch80
|
|
3/8”x Sch40
|
1-1/2”x Sch40
|
5”x Sch40
|
|
3/8”x Sch80
|
1-1/2”x Sch80
|
5”x Sch80
|
|
1/2”x Sch40
|
2”x Sch40
|
6”x Sch40
|
|
1/2”x Sch80
|
2”x Sch80
|
6”x Sch80
|
|
3/4”x Sch40
|
2-1/2”x Sch40
|
8”x Sch40
|
|
3/4”x Sch80
|
2-1/2”x Sch80
|
8”x Sch80
|
|
GB/T8162-1999（熱軋、擠(jǐ)壓、擴(kuò)管）
|
|
尺寸公差
|
|
标準
|
外徑公差
|
壁厚公差
|
|
GB/T8162-1999
|
D<50
|
±0.5mm
|
S≤4mm
|
±12.5%
|
|
D≥50
|
±1%
|
4mm<S≤20mm
|
+15/-12.5%
|
|
S>20mm
|
±12.5%
|
|
|
縱向力學性能
|
|
标準
|
綱級
|
抗拉強度(MPa)
|
屈服強(qiáng)度(MPa) ≥
|
延伸率(%)≥
|
|
≤16
|
>16-30mm
|
|
GB/T8163-1999
|
10
|
335
|
205
|
195
|
24
|
|
20
|
390
|
245
|
235
|
20
|
|
35
|
510
|
305
|
295
|
17
|
|
45
|
590
|
335
|
325
|
14
|
|
Q345
|
490
|
325
|
315
|
21
|
|
|
化學成份
|
|
标準
|
牌号
|
C
|
Si
|
Mn
|
P≤
|
S≤
|
Cu≤
|
Ni≤
|
Cr≤
|
Mo≤
|
V≤
|
|
GB/T8163-1999
|
10
|
0.07-0.03
|
0.17-0.37
|
0.35-0.65
|
0.035
|
0.035
|
0.25
|
0.30
|
0.15
|
/
|
/
|
|
20
|
0.17-0.23
|
0.17-0.37
|
0.35-0.65
|
0.035
|
0.035
|
0.25
|
0.30
|
0.25
|
/
|
/
|
|
35
|
0.32-0.39
|
0.17-0.37
|
0.50-0.80
|
0.035
|
0.035
|
0.25
|
0.30
|
0.25
|
/
|
/
|
|
45
|
0.42-0.50
|
0.17-0.37
|
0.50-0.80
|
0.035
|
0.035
|
0.25
|
0.30
|
0.25
|
/
|
/
|
|
16Mn
|
0.12-0.20
|
0.20-0.60
|
1.20-1.60
|
0.045
|
0.045
|
0.25
|
0.25
|
0.25
|
/
|
/
|
|
|
|
|
|
Q/CG46.2-1996（僅(jǐn)限熱擴(kuò)管）
|
|
結
構
用
管
|
|
|
标 準(zhǔn)
|
Q/CG46.2-1996
|
|
用 途
|
适用於(yú)結構用一般無縫(fèng)鋼管等
|
|
鋼(gāng)種(zhǒng)、标準
|
10、20、35、45、16Mn、合金結構(gòu)鋼(gāng)等，成分按GB699-88、GB/T1591-94
|
|
尺寸偏差
|
熱(rè)擴(kuò)管
|
D>351, 外徑(jìng)±1%， 壁厚±18%
|
|
彎(wān)曲度
|
≤3mm/m
|
|
力 學
性 能
|
鋼(gāng) 種(zhǒng)
|
σb
N/mm2
|
σs (N/mm2)
|
δs%
|
|
S<15
|
S>16 - 40
|
|
20
|
410-540
|
≥255
|
≥245
|
≥21
|
|
45
|
≥590
|
≥335
|
≥325
|
≥14
|
|
16Mn
|
≥490
|
≥325
|
≥315
|
≥21
|
|
水壓(yā)試(shì)驗
|
逐根進(jìn)行、最大壓力≤8MPa 供方可用渦流或超聲檢(jiǎn)驗代水壓試驗
|
|
壓(yā)扁試(shì)驗
|
D>315、且S≤10時，進(jìn)行壓扁試驗。10鋼(gāng)的α=0.09,20、35、45、低合金、合金鋼(gāng)的α=0.07
|
|
其它項(xiàng)目
|
|
|
備(bèi) 注
|
該(gāi)标準還包括35Cr、40Cr、12CrMo、35CrMo、12Cr1MoV、30CrMnSi等合金結構鋼，性能爲調(diào)質後性能。
|
|
|
|
管線(xiàn)管 API SPEC 5L
|
|
尺寸公差
|
|
标準
|
外徑公差
|
壁厚公差
|
|
A25.A.B
|
X42-X70
|
|
D<60.3
|
+0.41/-0.40mm
|
D<73
|
+20/-12.5%
|
D≥73
|
+15/-12.5%
|
|
API SPEC 5L
|
D≥60.3
|
+0.75/-0.40mm
|
D≥73
|
+15/-12.5%
|
D>73
|
+15/-12.5%
|
|
|
機械性能
|
|
标準
|
綱級
|
屈服強度(MPa)
|
抗拉強度(MPa)
|
延伸率
|
|
API SPEC 5L
|
PSL1
|
|
|
A25
|
172
|
310
|
|
A
|
207
|
331
|
|
B
|
241
|
414
|
|
X42
|
290
|
414
|
|
X46
|
317
|
434
|
|
X52
|
359
|
455
|
|
X56
|
386
|
490
|
|
X60
|
414
|
517
|
|
X65
|
448
|
531
|
|
X70
|
483
|
565
|
|
PSL2
|
|
|
Min
|
Max
|
Min
|
Max
|
|
B
|
241
|
448
|
414
|
758
|
|
X42
|
290
|
496
|
414
|
758
|
|
X46
|
317
|
524
|
434
|
758
|
|
X52
|
359
|
531
|
455
|
758
|
|
X56
|
386
|
544
|
490
|
758
|
|
X60
|
414
|
565
|
517
|
758
|
|
X65
|
448
|
600
|
531
|
758
|
|
X70
|
483
|
621
|
565
|
758
|
|
X80
|
552
|
690
|
621
|
827
|
|
|
化學成份
|
|
标準
|
鋼級
|
C
|
Mn
|
P
|
|
S
|
|
Max
|
Max
|
Min
|
Max
|
Max
|
|
API SPEC 5L
|
PSL1
|
|
A25II
|
0.21
|
0.60
|
|
0.030
|
0.030
|
|
A25III
|
0.21
|
0.60
|
0.45
|
0.80
|
0.030
|
|
A
|
0.22
|
0.90
|
|
0.030
|
0.030
|
|
B
|
0.28
|
1.20
|
|
0.030
|
0.030
|
|
X42
|
0.28
|
1.30
|
|
0.030
|
0.030
|
|
X46.X52.X56
|
0.28
|
1.40
|
|
0.030
|
0.030
|
|
X60.X65.X70
|
0.28
|
1.40
|
|
0.030
|
0.030
|
|
PSL2
|
|
B
|
0.24
|
1.20
|
|
0.025
|
0.015
|
|
X42
|
0.24
|
1.30
|
|
0.025
|
0.015
|
|
X46.X52.X56
|
0.24
|
1.40
|
|
0.025
|
0.015
|
|
X60.X65.X70.X80
|
0.24
|
1.40
|
|
0.025
|
0.015
|
|
|
|